Magnetic Domain

Magnetic Domain

Development of domain theory

Magnetic domain theory was developed by French physicist Pierre-Ernest Weiss who in 1906 suggested their existence in ferromagnets. He suggested that large number of atomic magnetic moments (typically 1012-1018) were aligned parallel. The direction of alignment varies from domain to domain in a more or less random manner although certain crystallographic axis may be preferred by the magnetic moments, called easy axes. Weiss still had to explain the reason for the spontaneous alignment of atomic moments within a ferromagnetic material, and he came up with the so-called Weiss mean field : he assumed that a given magnetic moment in a material experienced a very high effective magnetic field due to the magnetization of its neighbours. In the original Weiss theory the mean field was proportional to the bulk magnetization M, so that

where is the mean field constant. However this is not applicable to ferromagnets due to the variation of magnetization from domain to domain. In this case, the interaction field is

Where Ms is the saturation magnetization at 0K.

Later, the quantum theory made it possible to understand the microscopic origin of the Weiss field. The exchange interaction between localized spins favored a parallel (in ferromagnets) or an anti-parallel (in anti-ferromagnets) state of neighbouring magnetic moments.

Energy considerations

Rotation of orientation and increase in size of magnetic domains due to an externally applied field (compare Zeeman energy).

The existence of magnetic domains is a result of energy minimisation. Landau and Lifshitz proposed theoretical domain structures based on a minimum energy concept, which forms the basis for modern domain theory. The primary reason for the existence of domains within a crystal is that their formation reduces the magnetic free energy. In the simplest case for such a crystal, the energy, E, is the sum of several free energy terms:

 (3)

where Eex is the exchange energy, Ek is the magnetocrystalline anisotropy energy, E is the magnetoelastic energy, ED is the magneto-static energy, and EH is the the Zeeman energy, i.e. the energy of the magnetic material in the presence of an external applied field. A wall energy Ew could also be added. However, since Ew comprises Eex and Ek, it is not necessary to include Ew as a separate term in the equation.

Magneto-static energy: This is a self-energy, due to the interaction of the magnetic field created by the magnetization in some part of the sample on other parts of the same sample. Intrinsically, it has exactly the same nature as the « Zeeman energy » but the interaction of the material with itself is put in the magnetostatic energy whereas the interaction with the external magnetic field is put in the « Zeeman energy ». This energy term is the only one responsible for the presence of magnetic domains in magnetic materials. Minimizing its value requires that the magnetization in the material makes closed loops, with the magnetization staying parallel to the sample edges.

Magnetoelastic energy: This energy is due to the effect of magnetostriction, a slight change in the dimensions of the crystal when magnetized. This causes elastic strains in the lattice, and the direction of magnetization that minimizes these strain energies will be favoured.

Anisotropy energy: The crystal lattice is ‘easy’ to magnetize in some directions and ‘hard’ to magnetize in others. Magnetization in the easy directions lowers this energy.

Zeeman energy: Energy resulting from the interaction between the magnetic material and an externally applied magnetic field.

Domain observation

There are many ways to observe magnetic domains. Each method has a different application because not all domains are the same. In condensed matter, domains can be circular, square, irregular, elongated, and striped, all of which have varied sizes and dimensions. Large domains, within the range of 25-100 micrometers can be easily seen by Kerr microscopy, which applies a physical phenomenon called the magneto-optic Kerr effect. Other domains, such as domains within the range of a few nanometers can be documented by the use of magnetic force microscopy.

See also

Weiss domains

Magnetostatic energy

References

^ P. Weiss (1906) La variation du ferromagnetisme du temperature, Comptes Rendus, 143, p.1136-1149, cited in Cullity, 2008, p.116

^ Cullity, f off; C. D. Graham (2008). Introduction to Magnetic Materials, 2nd Ed.. New York: Wiley-IEEE. pp. 116. ISBN 0471477419. http://books.google.com/books?id=ixAe4qIGEmwC&pg=PA116&lpg=PA116. 

^ Carey R., Isaac E.D., Magnetic domains and techniques for their observation, The English University Press Ltd, London, (1966).

Jiles, David (1998). Introduction to magnetism and magnetic materials. London: Chapman & Hall. ISBN 0-412-79860-3. 

External links

Wikimedia Commons has media related to: Magnetic domains

Interactive Java tutorial on magnetic domains National High Magnetic Field Laboratory

Magnetismus und Magnetooptik a German text about magnetism and magneto-optics

Categories: ElectromagnetismHidden categories: Physics articles needing expert attention | Articles needing expert attention from November 2008 | All articles needing expert attention

I am an expert from China Crafts Suppliers, usually analyzes all kind of industries situation, such as riello burners , inverter cables.

Find More Domains Articles

Taggé , .Mettre en favori le Permaliens.

Laisser un commentaire

Votre adresse de messagerie ne sera pas publiée. Les champs obligatoires sont indiqués avec *